ICandelo le-NdFeB, lisetyenziswa ngokubanzi kwiinjini zombane

Inkcazelo emfutshane:

Icandelo Ndfeb zisetyenziswa ngokubanzi kwiimotor kunye nazo zonke iintlobo zezixhobo.Ukuthatha iintlobo ezahlukeneyo zeenjini njengomzekelo, ukusetyenziswa kweSegment Ndfeb kunezibonelelo zengxolo ephantsi kunye netorque ephezulu.Amabanga angentla kwe-SH yeCandelo le-Ndfeb asetyenziswa ikakhulu kwimarike ngoku.

Ibakala elingentla kwe-SH kwinkampani yethu esetyenziswa ngokubanzi ngentla kwe-non-dysprosium okanye itekhnoloji engaphantsi kwe-dysprosium kwinzuzo yeendleko zefomula iyabonakala.

Singenziwa ngokwezifiso ngokobukhulu obuchaziweyo bomthengi, i-arc blank, exazulula inkunkuma ye-square billet machining, iindleko eziphezulu njl. Kwangaxeshanye, sisebenzisa inkqubo yokungena kwe-arc yomgangatho ophantsi weemveliso ngokusebenzisa i-magnetron sputtering, vumela umhlaba onqabileyo onzima kakuhle- Umlinganiselo wokungena kumda wokuziinkozo kwisigaba semagnethi, okwenza ukuba ukutyabeka kuzinze ngakumbi kunenkqubo yokungena kwimarike ngoku ngaxeshanye, ukufikelela kumaxabiso aphantsi kumthengi.

Thumela i-imeyile kuthi

Iinkcukacha zeMveliso

Iithegi zeMveliso

Ngobungakanani, inkampani yethu ixhotyiswe ngomatshini wokuhlela ubungakanani be-arc ye-Keyence, enciphisa umngcipheko obangelwa yibhetshi embi yolawulo lokunyamezelana inxalenye yendibano yemagnethi yabathengi.

Kungakhathaliseki ukuba luhlobo luni lokutyabeka, sonke sinokuqinisekisa unyango olukhethekileyo lwe-arc kumphezulu wecandelo le-colloid affinity yemagnethi kwizisombululo kwinkqubo yokusetyenziswa apho intonga, ukunyanzeliswa kweglue edibeneyo ayanelanga kunye nokunye.
Kwimiqathango yonikezelo, sineendawo ezingenanto ezahlukeneyo ngobukhulu kunye namabakala, ukwenza imagnethi yeprototype nangaliphi na ixesha.Siodola umgubo ngobuninzi kwangaphambili ukuze itekhnoloji ye-alloy eguquguqukayo ikwazi ukwanelisa iimfuno zokuhanjiswa kwabathengi emva kokufumana imfuno yomthengi.

Inkampani yethu ixhotyiswe ngeqela lobuchwephesha kunye neqela lokuthengisa elinokubonelela ngeengcebiso zobuchwephesha, iskimu sokudityaniswa kwemagnethi, kunye nenani elikhulu lamatyala okusebenzisa nangaliphi na ixesha ukuqinisekisa ukuba akukho maxhala ongezelelweyo kwinkqubo yokusetyenziswa kwabathengi.

Sithobela ngokungqongqo imigangatho yolawulo lwenkqubo, ulawulo lokuqukuqela ngokuhambelana nenkqubo ye-IATF16949, ukuqinisekisa ukuhanjiswa kunye nokujongwa komgangatho kubathengi.

Inkqubo yeMveliso yeNdFeB

Ukwaleka Intshayelelo

Umphezulu	Ukwaleka	Ukutyeba μm	Umbala	Iiyure ze-SST	Iiyure zePCT
Nickel	Ni	10～20	Isilivere eqaqambileyo	>24 ukuya kutsho ku72	>24 ukuya kutsho ku72
Nickel	Ni+Cu+Ni	10～20	Isilivere eqaqambileyo	>24 ukuya kutsho ku72	>24 ukuya kutsho ku72
I-Nickel emnyama	Ni+Cu+Ni	10～20	Umnyama Oqaqambileyo	> 48-96	>48
Cr3+Zinc	Zn C-Zn	5 ～8	UBrighe Blue Umbala Oqaqambileyo	>16 -48 > 36 -72	---
Sn	Ni+Cu+Ni+Sn	10 ~ 25	Isilivere	> 36 -72	>48
Au	Ni+Cu+Ni+Au	10～15	Igolide	>12	>48
Ag	Ni+Cu+Ni+Ag	10 ~ 15	Isilivere	>12	>48
Epoxy	Epoxy	10～20	Mnyama / Grey	>48	---
	Ni+Cu+Epoxy	15 ~ 30		>72 ~108	---
	Zn+Epoxy	15 ~ 25		>72 ~108	---
Ukunyamezela	---	1～3	Grey emnyama	Ukhuseleko lwexeshana	---
Iphosphate	---	1～3	Grey emnyama	Ukhuseleko lwexeshana)	---

Iimpawu zoMzimba

Into	Iiparamitha	Ixabiso leReferensi	Iyunithi
I-Magnetic encedisayo Iipropati	I-Coefficient yoBubushushu obubuyiselwayo ye-Br	-0.08--0.12	%/℃
	I-Coefficient yoBubushushu obubuyiselwayo ye-Hcj	-0.42-0.70	%/℃
	Ubushushu obuthile	0.502	KJ ·(Kg ·℃)-1
	Ubushushu beCurie	310~380	℃
Mechanical Physical Iipropati	Ukuxinana	7.5~7.80	g/cm³
	Vickers Ukuqina	650	Hv
	Ukunyangwa koMbane	1.4x10-6	μQ · m
	Amandla acinezelayo	1050	MPa
	Tensile strength	80	Mpa
	Ukugoba Amandla	290	Mpa
	I-Thermal Conductivity	6 ukuya ku-8.95	W/m ·K
	Imodulus yolutsha	160	GPA
	Ukwandiswa kweThermal(C⊥)	-1.5	10-6/℃-1
	Ukwandiswa kweThermal(CII)	6.5	10-6/℃-1