Isicelo: Iringi ye-NdFeB isetyenziswa kakhulu kwimoto yekomityi engenanto, i-vacuum cleaner motor, i-hair dryer motor, isandisi-lizwi kunye nezinye iindawo.Kwizicelo zemoto, ineemfuno eziphezulu kakhulu kubungakanani bejometri yemagnethi kunye nepropathi yemagnethi, ukunyamezelana okuncinci kunokuba ngaphakathi kwe-0-0.03mm. Kwisicelo sesandisi-lizwi, umazibuthe uqhelekile kunye nokwaleka kwe-Zn, ukuhanjiswa phantsi kwemeko engenamagnetic, ibakala lemagnethi I-N, M kunye ne-H series grade, ngokwesiqhelo imagnethi yesandisi-lizwi ayifuni ibakala eliphezulu.Esinye isicelo sentengiso yokuthambisa, sibonelela ngezigidi zamaqhekeza ngemagnethi kubathengi bethu kwihlabathi liphela, iimagnethi zisetyenziselwa ukupakisha ibhokisi, i-axial magnetized. okanye multipole axial umazibuthe ezifana 2 okanye 4 iipali, kwaye hayi kuphela umazibuthe esulungekileyo, nathi avaialbe ezinye indibano umazibuthe.
Iimveliso ezenziwe ngokwezifiso: Imagnethi yethu ingenziwa ngokwezifiso ukusuka kwi-3mm-200mm ububanzi bangaphandle, i-1mm-150mm ububanzi obungaphakathi, ubukhulu ukusuka kwi-1mm-70mm.
Inkqubo yeMveliso yeNdFeB
Ukwaleka Intshayelelo
| Umphezulu | Ukwaleka | Ukutyeba μm | Umbala | Iiyure ze-SST | Iiyure zePCT | |
| Nickel | Ni | 10～20 | Isilivere eqaqambileyo | >24 ukuya kutsho ku72 | >24 ukuya kutsho ku72 | |
| Ni+Cu+Ni | ||||||
| I-Nickel emnyama | Ni+Cu+Ni | 10～20 | Umnyama Oqaqambileyo | > 48-96 | >48 | |
| Cr3+Zinc | Zn C-Zn | 5 ～8 | UBrighe Blue Umbala Oqaqambileyo | >16 -48 > 36 -72 | --- | |
| Sn | Ni+Cu+Ni+Sn | 10 ~ 25 | Isilivere | > 36 -72 | >48 | |
| Au | Ni+Cu+Ni+Au | 10～15 | Igolide | >12 | >48 | |
| Ag | Ni+Cu+Ni+Ag | 10 ~ 15 | Isilivere | >12 | >48 | |
| Epoxy | Epoxy | 10～20 | Mnyama / Grey | >48 | --- | |
| Ni+Cu+Epoxy | 15 ~ 30 | >72 ~108 | --- | |||
| Zn+Epoxy | 15 ~ 25 | >72 ~108 | --- | |||
| Ukunyamezela | --- | 1～3 | Grey emnyama | Ukhuseleko lwexeshana | --- | |
| Iphosphate | --- | 1～3 | Grey emnyama | Ukhuseleko lwexeshana) | --- | |
Iimpawu zoMzimba
| Into | Iiparamitha | Ixabiso leReferensi | Iyunithi |
| I-Magnetic encedisayo Iipropati | I-Coefficient yoBubushushu obubuyiselwayo ye-Br | -0.08--0.12 | %/℃ |
| I-Coefficient yoBubushushu obubuyiselwayo ye-Hcj | -0.42-0.70 | %/℃ | |
| Ubushushu obuthile | 0.502 | KJ ·(Kg ·℃)-1 | |
| Ubushushu beCurie | 310~380 | ℃ | |
| Mechanical Physical Iipropati | Ukuxinana | 7.5~7.80 | g/cm3 |
| Vickers Ukuqina | 650 | Hv | |
| Ukunyangwa koMbane | 1.4x10-6 | μQ · m | |
| Amandla acinezelayo | 1050 | MPa | |
| Tensile strength | 80 | Mpa | |
| Ukugoba Amandla | 290 | Mpa | |
| I-Thermal Conductivity | 6 ukuya ku-8.95 | W/m ·K | |
| Imodulus yolutsha | 160 | GPA | |
| Ukwandiswa kweThermal(C⊥) | -1.5 | 10-6/℃-1 | |
| Ukwandiswa kweThermal(CII) | 6.5 | 10-6/℃-1 |
Umboniso Wemifanekiso